Effect of the initial particle size distribution on the properties of suspension plasma sprayed Al2O3-TiO2 coatings
Ver/ Abrir
Impacto
Scholar |
Otros documentos de la autoría: Vicent Cabedo, Mónica; Bannier, Emilie; Carpio Cobo, Pablo; Rayón, E.; Benavente, Rut; Salvador Moya, María Dolores; Sánchez-Vilches, Enrique
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7033
comunitat-uji-handle3:10234/8618
comunitat-uji-handle4:
INVESTIGACIONMetadatos
Título
Effect of the initial particle size distribution on the properties of suspension plasma sprayed Al2O3-TiO2 coatingsAutoría
Fecha de publicación
2015-04Editor
ElsevierCita bibliográfica
VICENT, M., et al. Effect of the initial particle size distribution on the properties of suspension plasma sprayed Al 2 O 3–TiO 2 coatings. Surface and Coatings Technology, 2015, vol. 268, p. 209-215.Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://www.sciencedirect.com/science/article/pii/S0257897214011426Versión
info:eu-repo/semantics/acceptedVersionPalabras clave / Materias
Resumen
Al2O3–TiO2 coatings have been deposited by atmospheric plasma spraying from agglomerated, nanostructured powders showing better properties than those of their conventional (microstructured) counterparts. These nanos ... [+]
Al2O3–TiO2 coatings have been deposited by atmospheric plasma spraying from agglomerated, nanostructured powders showing better properties than those of their conventional (microstructured) counterparts. These nanostructured coatings can be also obtained by suspension plasma spraying however the research on suspension plasma sprayed Al2O3–TiO2 is still scarce. Consequently, it is crucial to study the effect of the suspension characteristics on the coating properties and to optimize the deposition process.
In this work, Al2O3–13 wt.% TiO2 tribological coatings were successfully deposited by suspension plasma spraying from three different feedstocks: a nanometric suspension and two bimodal suspensions with different solid contents made up of titania nanoparticles and alumina submicron-sized particles. The coating microstructure and phase composition were characterized using scanning electron microscopy and X-ray diffraction analysis. Moreover, nanoindentation technique was used to determine the nanomechanical properties of coatings.
The influence of the feed suspension characteristics on the final coating quality was analyzed. Findings showed that similar microstructures and phases were developed after depositing the different feedstocks. In addition suspension feedstock made up of nanoparticles resulted in a coating with better mechanical properties. However the use of submicron-sized particles in the suspension feedstocks gives rise to some technical and economic advantages in the process which should be taken into account when a suspension plasma spraying process is to be set up. [-]
Publicado en
Surface and Coatings Technology Volume 268, 25 April 2015Derechos de acceso
Copyright © 2014 Elsevier B.V. All rights reserved.
info:eu-repo/semantics/openAccess
info:eu-repo/semantics/openAccess
Aparece en las colecciones
- QUI_Articles [300]