Hardness and Young's modulus distributions in atmospheric plasmas prayed WC–Co coatings using nanoindentation
Impacto
Scholar |
Otros documentos de la autoría: Rayón, E.; Bonache Bezares, Victoria; Salvador Moya, María Dolores; Roa, J. J.; Sánchez-Vilches, Enrique
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7033
comunitat-uji-handle3:10234/8618
comunitat-uji-handle4:
INVESTIGACIONEste recurso está restringido
http://dx.doi.org/10.1016/j.surfcoat.2011.03.012 |
Metadatos
Título
Hardness and Young's modulus distributions in atmospheric plasmas prayed WC–Co coatings using nanoindentationAutoría
Fecha de publicación
2011-05-25Editor
ElsevierISSN
0257-8972Cita bibliográfica
Surface and Coatings Technology (May 2011), Vol. 205, no. 17-18, p. 4192-4197Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://www.sciencedirect.com/science/article/pii/S0257897211001903Palabras clave / Materias
Resumen
A statistical indentation analysis of WC–Co coatings obtained by atmospheric plasma spray (APS) with two secondary plasma gases, H2 and He, was investigated using an instrumented indentation technique with the aim of ... [+]
A statistical indentation analysis of WC–Co coatings obtained by atmospheric plasma spray (APS) with two secondary plasma gases, H2 and He, was investigated using an instrumented indentation technique with the aim of correlating the influence of the nanomechanical behaviour of each constituent phase with the micromechanical characteristics of these coatings.
X-ray diffraction (XRD) and backscattered electron (BSE) analysis showed that H2 gas produced a greater decarburisation of the WC phase. The dissolution and decomposition of the WC phase during the process produced a Co + W+C solid solution as binder phase and the formation of W2C and W as secondary phases. The nanohardness (H) and Young'smodulus (E) resulting from a grid of 300 indentations performed at 50 nm in depth identified the characteristics of each phase in the heterogeneous structure produced by decarburisation. Statistical study by a CDF fit and Gaussian simulated distributions showed that the mechanical properties of the coatings were governed by the binder phase content, which decreased the possible hardening effect of the arising hardest phases (W2C and Co+W + C solid solution). [-]
Derechos de acceso
© 2011 Elsevier Inc. All rights reserved
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Aparece en las colecciones
- QUI_Articles [299]