Sinter-crystallisation kinetics of a SiO2–Al2O3–CaO–MgO–SrO glass-ceramic glaze
![Thumbnail](/xmlui/bitstream/handle/10234/186546/Encarna_Blasco_Roca.pdf.jpg?sequence=4&isAllowed=y)
Ver/ Abrir
Impacto
![Google Scholar](/xmlui/themes/Mirage2/images/uji/logo_google.png)
![Microsoft Academico](/xmlui/themes/Mirage2/images/uji/logo_microsoft.png)
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7033
comunitat-uji-handle3:10234/8618
comunitat-uji-handle4:
INVESTIGACIONMetadatos
Título
Sinter-crystallisation kinetics of a SiO2–Al2O3–CaO–MgO–SrO glass-ceramic glazeAutoría
Fecha de publicación
2020-03-15Editor
ElsevierCita bibliográfica
AMORÓS, J. L., et al. Sinter-crystallisation kinetics of a SiO2–Al2O3–CaO–MgO–SrO glass-ceramic glaze. Journal of Non-Crystalline Solids, 2020, 532: 119900.Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
https://www.sciencedirect.com/science/article/pii/S002230932030017X#!Versión
info:eu-repo/semantics/acceptedVersionPalabras clave / Materias
Resumen
This paper examines the microstructural development and kinetics of the sintering and crystallisation processes of a SiO2–Al2O3–RO (R = Ca, Mg, Sr) glass-ceramic glaze. Crystallisation and sintering kinetics were ... [+]
This paper examines the microstructural development and kinetics of the sintering and crystallisation processes of a SiO2–Al2O3–RO (R = Ca, Mg, Sr) glass-ceramic glaze. Crystallisation and sintering kinetics were studied by DTA and HSM, respectively, at different heating rates. The kinetic parameters of crystallisation were determined by the usual methods (Kissinger, Kissinger-Akahira-Sunose, Ozawa and Augis-Bennet methods), and the Johnson–Mehl–Avrami–Kolmogorov (JMAK) model, with an Avrami index of n = 3, characteristic of the surface crystallisation of very fine glass particles, was found to describe crystallisation kinetics very well. Sintering could also be described by the JMAK model, but with n < 1. Assuming the effect of temperature on the sintering rate to be the same as that of this variable on the inverse of glass matrix viscosity, a model was developed, based on the JMAK model, which only required a single fitting parameter. As the heating rate increased, the degree of overlap between the sintering and crystallisation processes was verified to decrease. [-]
Derechos de acceso
© 2020 Elsevier B.V. All rights reserved.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
Aparece en las colecciones
- QUI_Articles [296]