Beige materials for the ceramic industry: AlxVyFe1-xP1-yO4 (0.0 ≤ x ≤ 0.3, 0.0 ≤ y ≤ 0.1) solid solutions
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONEste recurso está restringido
0272-8842 |
https://doi.org/10.1016/j.ceramint.2019.01.133 |
Metadatos
Título
Beige materials for the ceramic industry: AlxVyFe1-xP1-yO4 (0.0 ≤ x ≤ 0.3, 0.0 ≤ y ≤ 0.1) solid solutionsAutoría
Fecha de publicación
2019-05Editor
ElsevierCita bibliográfica
TENA, M. A., et al. Beige materials for the ceramic industry: AlxVyFe1-xP1-yO4 (0.0≤ x≤ 0.3, 0.0≤ y≤ 0.1) solid solutions. Ceramics International, 2019, vol. 45, no 7, p. 8271-8278.Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
https://www.sciencedirect.com/science/article/pii/S0272884219301634#!Versión
info:eu-repo/semantics/publishedVersionPalabras clave / Materias
Resumen
AlxVyFe1-xP1-yO4 (0.0 ≤ x ≤ 0.3, 0.0 ≤ y ≤ 0.1) compositions were synthesized via the chemical co-precipitation method. At 500 °C, α-FePO4 berlinite crystallizes together with FePO4 tridymite, Fe(III) occupying ... [+]
AlxVyFe1-xP1-yO4 (0.0 ≤ x ≤ 0.3, 0.0 ≤ y ≤ 0.1) compositions were synthesized via the chemical co-precipitation method. At 500 °C, α-FePO4 berlinite crystallizes together with FePO4 tridymite, Fe(III) occupying tetrahedral sites in both structures. The variation in the unit cell confirms the formation of solid solutions with α-FePO4 berlinite structure. These AlxVyFe1-xP1-yO4 (0.0 ≤ x ≤ 0.3, 0.0 ≤ y ≤ 0.1) solid solutions are stable between 800 and 1000 °C and when x > 0.2 at 1200 °C. Fe7P6O24 with Fe(II) and Fe(III) is detected in the compositions with the highest amount of Fe(III) at 1200 °C. The materials are paramagnetic between 100 and 300 K and the variation in their magnetic susceptibilities fits the Curie-Weiss law with negative Weiss constants (antiferromagnetism). At 1200 °C, the presence of small amounts of Fe(II) is associated with a slight decrease in μeff. The presence of vanadium in samples (y > 0) decreases their μeff. Optimal beige materials to work without sample fusion at 1200 °C are reported. [-]
Publicado en
Ceramics International, 2019, vol. 45, no 7Proyecto de investigación
Ministerio de Ciencia, Innovación y Universidades: projects MAT2013-40950-R, MAT2016-78155-C2-1-R; ERDF fundingDerechos de acceso
Copyright © Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Aparece en las colecciones
- QUIO_Articles [702]