Effect of fluorine and nitrogen content on the properties of Ca-Mg-Si-Al-O-(N)-(F) glasses
Visualitza/
Impacte
Scholar |
Altres documents de l'autoria: García Bellés, Àngel R.; Clausell-Terol, Carolina; Barba-Juan, Antonio; Pomeroy, M. J.; Hampshire, S.
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7033
comunitat-uji-handle3:10234/8618
comunitat-uji-handle4:
INVESTIGACIONMetadades
Títol
Effect of fluorine and nitrogen content on the properties of Ca-Mg-Si-Al-O-(N)-(F) glassesAutoria
Data de publicació
2017Editor
ElsevierISSN
0272-8842; 1873-3956Cita bibliogràfica
GARCÍA-BELLÉS, Á. R., et al. Effect of fluorine and nitrogen content on the properties of Ca-Mg-Si-Al-O-(N)-(F) glasses. Ceramics International, 2017, vol. 43, no 5, p. 4197-4204.Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://www.sciencedirect.com/science/article/pii/S0272884216322970Versió
info:eu-repo/semantics/submittedVersionParaules clau / Matèries
Resum
X-ray amorphous glasses of composition (in equivalent percent) 15Ca:15Mg: 55Si:15Al:(100-x-y)O:xN:yF with x=0, 10, 15 and y=0, 1, 3, 5, were prepared by melting and casting. The effects of oxygen substitution by ... [+]
X-ray amorphous glasses of composition (in equivalent percent) 15Ca:15Mg: 55Si:15Al:(100-x-y)O:xN:yF with x=0, 10, 15 and y=0, 1, 3, 5, were prepared by melting and casting. The effects of oxygen substitution by fluorine and/or nitrogen on the physical, mechanical, thermal and optical properties of the glasses have been investigated. Molar volume, fractional glass compactness, microhardness, Young's Modulus, glass-transition temperature, dilatometric-softening point and refractive index increased linearly with nitrogen substitution for oxygen, whereas molar volume and thermal expansion coefficient decreased linearly with nitrogen increase. In contrast, all properties except glass-transition temperature and dilatometric-softening point, are virtually unaffected by fluorine substitution for oxygen. Significant and linear, decreases in thermal properties occurred with increasing fluorine substitution level. All the data collected and its analysis clearly showed that the substitution effects of fluorine for oxygen on the studied properties of the glasses of the system with general formula Ca-Mg-Si-Al-O-(N)-(F) are totally independent and additive with respect to the substitution effects of nitrogen for oxygen on glass properties. [-]
Publicat a
Ceramics International, 2017, vol. 43, no 5Drets d'accés