Structural characterization and colour of Ni3VxP2−xO8 (0 ≤ x ≤ 2) and Ni2VyP2−yO7 (0 ≤ y ≤ 2) materials
Ver/ Abrir
Impacto
Scholar |
Otros documentos de la autoría: Tena, M. A.; Mendoza, Rafael; García, José R.; Garcia-Granda, Santiago
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONMetadatos
Título
Structural characterization and colour of Ni3VxP2−xO8 (0 ≤ x ≤ 2) and Ni2VyP2−yO7 (0 ≤ y ≤ 2) materialsFecha de publicación
2017Editor
ElsevierISSN
2211-3797Cita bibliográfica
TENA, M. A., et al. Structural characterization and colour of Ni 3 V x P 2− x O 8 (0≤ x≤ 2) and Ni 2 V y P 2− y O 7 (0≤ y≤ 2) materials. Results in Physics, 2017Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://www.sciencedirect.com/science/article/pii/S2211379717300220Versión
info:eu-repo/semantics/publishedVersionPalabras clave / Materias
Resumen
Structural characterization of Ni3VxP2−xO8 (0 ≤ x ≤ 2) and Ni2VyP2−yO7 (0 ≤ y ≤ 2) compositions was made and colour parameters of these materials measured. Ni(II) diphosphate and divanadate crystalline phases are not ... [+]
Structural characterization of Ni3VxP2−xO8 (0 ≤ x ≤ 2) and Ni2VyP2−yO7 (0 ≤ y ≤ 2) compositions was made and colour parameters of these materials measured. Ni(II) diphosphate and divanadate crystalline phases are not stables at high temperature. Solid solutions in Ni3P2O8 and Ni3V2O8 are obtained by incorporation of V(V) in Ni orthophosphate and P(V) in Ni orthovanadate structures. Solid solutions with Ni3V2O8 structure are formed in a greater compositional interval than solid solutions with Ni3P2O8 structure. These materials might be used as ceramic pigments because of its thermal and chemical stability. Tan brown colorations were obtained in glazed tiles when the fired compositions were 4% weight enamelled with a commercial glaze. [-]
Publicado en
Results in Physics, 2017, vol. 7Derechos de acceso
info:eu-repo/semantics/openAccess
Aparece en las colecciones
- QUIO_Articles [692]
El ítem tiene asociados los siguientes ficheros de licencia: