Influence of the activator concentration and calcium hydroxide addition on the properties of alkali-activated porcelain stoneware
Impacto
Scholar |
Otros documentos de la autoría: Reig, Lucía; Soriano, Lourdes; Borrachero, Mª Victoria; Monzó, J.; PAYÁ, JORDI
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7035
comunitat-uji-handle3:10234/8617
comunitat-uji-handle4:
INVESTIGACIONEste recurso está restringido
http://dx.doi.org/10.1016/j.conbuildmat.2014.04.023 |
Metadatos
Título
Influence of the activator concentration and calcium hydroxide addition on the properties of alkali-activated porcelain stonewareFecha de publicación
2014-07Editor
ElsevierISSN
0950-0618Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://www.sciencedirect.com/science/article/pii/S0950061814003407Palabras clave / Materias
Resumen
Objective
The aim of this research was to investigate the influence of the alkali activator concentration and calcium dosage on the fresh behavior, compressive strength and microstructure of the binder produced by ... [+]
Objective
The aim of this research was to investigate the influence of the alkali activator concentration and calcium dosage on the fresh behavior, compressive strength and microstructure of the binder produced by the alkali activation of porcelain stoneware waste, using NaOH and sodium silicate solution as activators.
Materials
Porcelain stoneware waste, NaOH and sodium silicate.
Method
Tested properties of mortars were the compressive strength and the setting times. Thermogravimetric analyses, microscopic studies, pH measurements, XRD and FTIR tests were used to assess the evolution of the microstructure developed.
Results
The results show that the activator concentration and calcium to sodium molar ratio strongly influence the fresh behavior and the hardening process of mortars. A linear evolution of compressive strength with sodium addition was observed when keeping the SiO2 concentration constant. Mortar samples with up to 36 MPa under compression were obtained after curing for 7 days at 65 °C. [-]
Publicado en
Construction and Building Materials, 2014, vol. 63Derechos de acceso
Copyright © 2014 Elsevier Ltd. All rights reserved.
Copyright © 2015 Elsevier B.V. or its licensors or contributors. ScienceDirect® is a registered trademark of Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Aparece en las colecciones
- EMC_Articles [831]