Effect of the recycling and annealing on the mechanical and fracture properties of poly(lactic acid)
Impacte
Scholar |
Altres documents de l'autoria: Nascimento, Lori Miller; Gamez-Perez, Jose; Santana Pérez, Orlando Onofre; Velasco, José Ignacio; Maspoch, Maria Lluïsa; Franco Urquiza, Edgar A.
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7034
comunitat-uji-handle3:10234/8619
comunitat-uji-handle4:
INVESTIGACIONAquest recurs és restringit
http://dx.doi.org/10.1007/s10924-010-0229-5 |
Metadades
Títol
Effect of the recycling and annealing on the mechanical and fracture properties of poly(lactic acid)Autoria
Data de publicació
2010Editor
Springer USTipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://link.springer.com/article/10.1007/s10924-010-0229-5Paraules clau / Matèries
Resum
The aim of this work is to evaluate the use of Poly(lactic acid) (PLA) industrial waste as a source of raw material for certain applications, as well as to understand the effects of the annealing on the fracture ... [+]
The aim of this work is to evaluate the use of Poly(lactic acid) (PLA) industrial waste as a source of raw material for certain applications, as well as to understand the effects of the annealing on the fracture behavior of PLA. PLA waste has been simulated by an initial step of extrusion in a single screw extruder and pelletizing. Specimens of virgin and reprocessed PLA were obtained by injection molding. An annealing treatment capable of increasing the percentage of crystallinity (determined by differential scanning calorimetry) was also analyzed in reprocessed and non reprocessed specimens. The fracture behavior was studied at slow and high testing speed, applying the linear elastic fracture mechanics (LEFM) on single edge notched bend (SENB) specimens. This study revealed that the fracture toughness of the reprocessed PLA was basically the same that the virgin PLA and also that the increase in the crystalline fraction produced an improvement on the fracture toughness, at slow loading rate. [-]
Publicat a
Journal of Polymers and the Environment December, 18, 4, p. 654-660Drets d'accés
Copyright 2010 Springer Science+Business Media
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Apareix a les col.leccions
- ESID_Articles [465]