Influence of processing on the ethylene-vinyl alcohol (EVOH) properties: Application of the successive self-nucleation and annealing (SSA) technique
![Thumbnail](/xmlui/bitstream/handle/10234/32120/46891.pdf.jpg?sequence=4&isAllowed=y)
View/ Open
Impact
![Google Scholar](/xmlui/themes/Mirage2/images/uji/logo_google.png)
![Microsoft Academico](/xmlui/themes/Mirage2/images/uji/logo_microsoft.png)
Metadata
Show full item recordcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7034
comunitat-uji-handle3:10234/8619
comunitat-uji-handle4:
INVESTIGACIONMetadata
Title
Influence of processing on the ethylene-vinyl alcohol (EVOH) properties: Application of the successive self-nucleation and annealing (SSA) techniqueAuthor (s)
Date
2010Publisher
Budapest University of TechnologyISSN
1788-618XBibliographic citation
eXPRESS Polymer Letters (2010) vol. 4, no. 3, p. 153–160Type
info:eu-repo/semantics/articlePublisher version
http://www.expresspolymlett.com/Subject
Abstract
Films of EVOH copolymers, processed three times by twin-screw extrusion were prepared using a cast-film line. The variation on the melt flow rate (MFR) and rheological behaviour of the films were determined, as well ... [+]
Films of EVOH copolymers, processed three times by twin-screw extrusion were prepared using a cast-film line. The variation on the melt flow rate (MFR) and rheological behaviour of the films were determined, as well as the thermal properties assessed by differential scanning calorimetry (DSC) and dynamic-mechanical thermal analysis (DMTA). As the results showed that the reprocessing induced an increase in the viscosity and orientation of the films, it was suggested that structural modifications from chain-extension or cross-linking reactions promoted by hydroxyl and residual acetoxyl groups, could be occurring. The successive self-nucleation and annealing (SSA) technique was applied, evidencing the structural modifications on the EVOH copolymer. [-]
Rights
http://rightsstatements.org/vocab/CNE/1.0/
© Budapest University of Technology
info:eu-repo/semantics/openAccess
© Budapest University of Technology
info:eu-repo/semantics/openAccess
This item appears in the folowing collection(s)
- ESID_Articles [477]