Combustion synthesis, structural and magnetic characterization of Ce1-xPrxO2 system
Impacte
Scholar |
Altres documents de l'autoria: Cruz Pacheco, Andrés Felipe; Gómez-Cuaspud, Jairo. A.; parra vargas, carlos arturo; Carda Castelló, Juan Bautista
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONAquest recurs és restringit
https://doi.org/10.1007/s10854-017-7546-6 |
Metadades
Títol
Combustion synthesis, structural and magnetic characterization of Ce1-xPrxO2 systemAutoria
Data de publicació
2017-07Editor
SpringerCita bibliogràfica
Cruz Pacheco, A.F., Gómez Cuaspud, J.A., Parra Vargas, C.A. et al. J Mater Sci: Mater Electron (2017) 28: 16358. https://doi.org/10.1007/s10854-017-7546-6Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
https://link.springer.com/article/10.1007/s10854-017-7546-6#Abs1Versió
info:eu-repo/semantics/publishedVersionParaules clau / Matèries
Resum
The current work describes the synthesis of Ce1−xPrxO2 (x = 0.0, 0.2, 0.4, 0.6, 0.8) and Pr6O11 systems by the combustion method, using citric acid as chelating agent. The obtained solids after combustion and calcination ... [+]
The current work describes the synthesis of Ce1−xPrxO2 (x = 0.0, 0.2, 0.4, 0.6, 0.8) and Pr6O11 systems by the combustion method, using citric acid as chelating agent. The obtained solids after combustion and calcination processes were characterized by thermal analysis (TGA-DTA) and infrared spectroscopy (FT-IR) to evaluate the chemical process during the combustion reaction. The surface area analysis using isotherms of nitrogen adsorption, reveal that all samples exhibit values between 70 and 135 m2 g−1, with a pore volume that allows its classification as mesoporous materials. The structural analysis by X-ray diffraction (XRD) and Rietveld refinement, revealed the obtention of a pure cubic structure Fm3m (225) along all cerium oxide modifications with nanocrystalline domain sizes, except for the praseodymium oxide that shows two crystalline phases in a monoclinic crystalline phase P121/c 1 (14) in the case of Pr6O11 and a cubic phase Fm3m (225) for PrO2 oxide. The oxygen storage capacity measurements performed in all samples, demonstrate that exchange of Ce ions by Pr increases the storage capacity of samples over the reference values in accordance with the synthesis method. The characterization by high-resolution transmission electron microscopy, confirmed that the solids are composed by nanometric aggregates with d spacing between 0.29 and 0.31 nm along main diffraction signals, in accordance with the experimental XRD results. Finally, the magnetic characterization in a ZFC configuration and a M-H mode, shows a strong paramagnetic behavior in all systems except in CeO2 oxide, which exhibited a prevalent diamagnetic behavior. [-]
Drets d'accés
© Springer Science+Business Media, LLC 2017
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Apareix a les col.leccions
- QUIO_Articles [701]