Characterization of polyhydroxyalkanoate blends incorporating unpurified biosustainably produced poly(3-hydroxybutyrate-co-3- hydroxyvalerate)
Visualitza/
Impacte
Scholar |
Altres documents de l'autoria: Martínez Abad, Antonio; Cabedo, Luis; Oliveira, Catalina S.S.; hilliou, loic; Reis, Maria; LAGARON, Jose
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7034
comunitat-uji-handle3:10234/8619
comunitat-uji-handle4:
INVESTIGACIONMetadades
Títol
Characterization of polyhydroxyalkanoate blends incorporating unpurified biosustainably produced poly(3-hydroxybutyrate-co-3- hydroxyvalerate)Autoria
Data de publicació
2015-07Editor
© 2015 Wiley Periodicals, Inc.Cita bibliogràfica
MARTÍNEZ‐ABAD, Antonio, et al. Characterization of polyhydroxyalkanoate blends incorporating unpurified biosustainably produced poly (3‐hydroxybutyrate‐co‐3‐hydroxyvalerate). Journal of Applied Polymer Science, 2016, 133.2.Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://onlinelibrary.wiley.com/doi/10.1002/app.42633/fullParaules clau / Matèries
Resum
ly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) produced by mixed bacterial cultures derived from a cheese whey (CW) industrial by-product (unpurified PHBV; u-PHBV) was incorporated into commercial PHBV without ... [+]
ly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) produced by mixed bacterial cultures derived from a cheese whey (CW) industrial by-product (unpurified PHBV; u-PHBV) was incorporated into commercial PHBV without previous purification or isolation processes. The presence of certain impurities was evident as investigated by scanning electron microscopy. The crystallinity of the polymer fraction was decreased by about 3% compared to the commercial PHBV. The onset of thermal degradation was not substantially affected by the incorporation of the u-PHBV fraction. A higher flexibility and elongation at break was mostly attributed to the increased contents in 3-hydroxyvalerate in the blends with increasing u-PHBV content. Water and D-limonene vapor permeability were not affected up to u-PHBV contents of 15 wt %. This study puts forth the potential use of unpurified PHBV obtained from mixed microbial cultures and grown from industrial by-products as a cost-effective additive to develop more affordable and waste valorized packaging articles [-]
Publicat a
Journal of Applied Polymer Science, Volume 133, Issue 2 January 10, 2016Drets d'accés
http://rightsstatements.org/vocab/CNE/1.0/
info:eu-repo/semantics/openAccess
info:eu-repo/semantics/openAccess
Apareix a les col.leccions
- ESID_Articles [465]