Influence of calcium aluminate cement (CAC) on alkaline activation of red clay brick waste (RCBW)
Visualitza/
Impacte
Scholar |
Altres documents de l'autoria: Reig, Lucía; Soriano, Lourdes; Borrachero, Mª Victoria; Monzó, J.; PAYÁ, JORDI
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7035
comunitat-uji-handle3:10234/8617
comunitat-uji-handle4:
INVESTIGACIONMetadades
Títol
Influence of calcium aluminate cement (CAC) on alkaline activation of red clay brick waste (RCBW)Data de publicació
2016-01Editor
ElsevierISSN
0958-9465Cita bibliogràfica
REIG, L., et al. Influence of calcium aluminate cement (CAC) on alkaline activation of red clay brick waste (RCBW). Cement and Concrete Composites, 2016, vol. 65, p. 177-185.Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://www.sciencedirect.com/science/article/pii/S0958946515300482Paraules clau / Matèries
Resum
In this paper, the effect of calcium aluminate cement (CAC) additions on the alkali activation of red clay brick waste (RCBW) was studied at room temperature and at 65 °C. RCBW was partially replaced with CAC (0–50 ... [+]
In this paper, the effect of calcium aluminate cement (CAC) additions on the alkali activation of red clay brick waste (RCBW) was studied at room temperature and at 65 °C. RCBW was partially replaced with CAC (0–50 wt.%) and blends were activated with NaOH and sodium silicate solutions. The compressive strength evolution was tested on mortars and the nature of the reaction products was analysed by infrared spectroscopy, X-ray diffraction, thermogravimetric analysis, microscopic studies and pH measurements. The results show that the use of CAC accelerates the activation process of RCBW so that 50 MPa were obtained in the blended mortars containing 40 wt.% CAC cured for 3 days at room temperature. CAC did not undergo normal hydration and only the C3AH6 phase was identified in the pastes blended with more than 30 wt.% CAC and cured at 65 °C, while the main reaction product was a cementitious gel containing Ca and Al from CAC. [-]
Publicat a
Cement and Concrete Composites, 2016, vol. 65Drets d'accés
Copyright © 2016 Elsevier B.V. or its licensors or contributors
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
Apareix a les col.leccions
- EMC_Articles [813]