Estudio de mejora de un vidriado brillante para baldosas de revestimiento por vía seca que reduzca sus defectos superficiales
View/ Open
Metadata
Show full item recordcomunitat-uji-handle:10234/158176
comunitat-uji-handle2:10234/71345
comunitat-uji-handle3:10234/107499
comunitat-uji-handle4:
TFG-TFMThis resource is restricted
Metadata
Title
Estudio de mejora de un vidriado brillante para baldosas de revestimiento por vía seca que reduzca sus defectos superficialesAuthor (s)
Tutor/Supervisor
Moreno Berto, ArnaldoTutor/Supervisor; University.Department
Universitat Jaume I. Departament d'Enginyeria QuímicaDate
2015-07-02Publisher
Universitat Jaume IAbstract
En el presente trabajo se lleva a cabo el estudio de los posibles fenómenos que rigen la aparición en mayor o menor medida del defecto de grieta y recogido a partir de las propiedades del esmalte en las baldosas de ... [+]
En el presente trabajo se lleva a cabo el estudio de los posibles fenómenos que rigen la aparición en mayor o menor medida del defecto de grieta y recogido a partir de las propiedades del esmalte en las baldosas de revestimiento que se fabrican en una planta con preparación de pasta vía seca de la Organización Corona. Se parte de la caracterización del defecto, confirmando que proviene desde el soporte y asociado a las características del proceso de preparación pasta. Posteriormente, se realiza la caracterización cerámica de los esmaltes que se utilizan en el proceso con el fin de relacionar los posibles hallazgos tanto de sus propiedades en crudo como en cocido con la información estadística que denota que el esmalte blanco en particular presenta un mejor comportamiento ante la aparición del defecto. En cuanto a las propiedades en crudo no fue posible encontrar una correlación entre los resultados de las propiedades medidas y el comportamiento de los esmaltes en planta, por lo cual se aborta este camino. En cuanto a las propiedades en cocido, se evaluaron los esmaltes de referencia vía microscopía de calefacción y se encontró que el esmalte blanco empieza a sinterizar bastante más pronto que la cristalina y que posiblemente por formar fase líquida móvil de forma prematura, se tienda a tapar las grietas que se generan desde procesos anteriores. En el caso del esmalte corte se presenta un comportamiento parecido al del blanco a pesar de tener una composición química bastante similar a la de la cristalina y que no fue posible explicar a partir de la composición por óxidos, razón por la cual se plantearon dos hipótesis para intentar justificar su comportamiento, encontrando de manera preliminar que aparentemente el ZrO2 podría actuar como fundente a baja temperatura. A partir de los hallazgos encontrados se reformuló la cristalina modificando óxidos alcalinos, alcalinotérreos y ZnO, buscando una sinterización más parecida a la del blanco, con formación de fase líquida prematura y menor viscosidad a baja temperatura, lo cual fue encontrado satisfactoriamente en los ensayos 1122-5, 1122-6 y 1122-9, de los cuales se eligieron los dos primeros para posteriores pruebas a nivel semi-industrial. Se fritaron a nivel industrial en Colombia las dos fritas correspondientes a los esmaltes elegidos y se tienen pendientes las pruebas semi-industriales que permitan concluir si las hipótesis planteadas van en la vía de lo esperado. [-]
In this work it is carried out the study of the possible phenomena that govern the appearance to a greater or lesser extent from the glaze properties of the crack defect in the wall tiles that are manufactured in a ... [+]
In this work it is carried out the study of the possible phenomena that govern the appearance to a greater or lesser extent from the glaze properties of the crack defect in the wall tiles that are manufactured in a factory with dry body powder preparation of Organización Corona. In the first part, the defect characterization was made, confirming that comes from the pressed body and is related with the dry preparation process. Subsequently, the characterization of ceramic glazes used in the process was made, in order to relate possible findings both of its green and during firing properties with statistical information that indicates that the “Blanco” glaze in particular has a better behavior in regards to the appearance of the defect. For green glaze properties it was not possible to find a correlation between the results of the measured properties and behavior of the glazes in the factory, therefore this path was aborted. For the properties of the glazes during firing, the reference glazes were evaluated with heating microscope and it was found that the “Blanco” glaze begins to sinter quite sooner than the “Cristalina” and possibly by forming liquid phase prematurely, it tends to cover the cracks generated from previous processes. For “Corte” glaze the behavior is similar to “Blanco” glaze despite having a fairly similar chemical composition to the “Cristalina” which could not be explained from the oxides composition, reason why two hypotheses were established to try to justify its behavior, finding preliminarily that apparently the ZrO2 could behave as a flux at low temperature. From the findings, the “Cristalina” glaze was reformulated by changing mainly the alkali, alkaline earth oxides and ZnO looking for a sintering curve more like the “Blanco” with premature liquid phase formation and lower viscosity at low temperature, what was found satisfactory in 1122-5, 1122-6 and 1122-9 trials, of which the first two were chosen for further tests at semi-industrial scale. The two frits that correspond to the chosen glazes were fritted at industrial scale in Colombia and its pending on the semi-industrial tests to figure out whether the hypotheses about crack generation are on way of the expected. [-]
Subject
Màster Universitari en Ciència, Tecnologia i Aplicacions dels Materials Ceràmics | Máster Universitario en Ciencia, Tecnología y Aplicaciones de los Materiales Cerámicos | Master's Degree in Ceramic Materials Science, Technology and Applications | defectos cerámicos | grieta | vidriados cerámicos | curva de sinterización | viscosidad de vidriados en fundido | ceramic defects | cracks | ceramic glazes | sintering curve | viscosity of melted glasses
Description
Treball Final de Màster Universitari en Ciència, Tecnologia i Aplicacions dels Materials Ceràmics (Pla de 2013). Codi: SIT024. Curs acadèmic 2014-2015