Effect of polyvinyl alcohol on the shape, photoluminescence and photocatalytic properties of PbMoO4 microcrystals
Impacte
![Google Scholar](/xmlui/themes/Mirage2/images/uji/logo_google.png)
![Microsoft Academico](/xmlui/themes/Mirage2/images/uji/logo_microsoft.png)
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7013
comunitat-uji-handle3:10234/8638
comunitat-uji-handle4:
INVESTIGACIONAquest recurs és restringit
http://dx.doi.org/10.1016/j.mssp.2014.05.027 |
Metadades
Títol
Effect of polyvinyl alcohol on the shape, photoluminescence and photocatalytic properties of PbMoO4 microcrystalsAutoria
Data de publicació
2014Editor
ElsevierISSN
1369-8001; 1873-4081Cita bibliogràfica
ARAÚJO, V. D., et al. Effect of polyvinyl alcohol on the shape, photoluminescence and photocatalytic properties of PbMoO 4 microcrystals. Materials Science in Semiconductor Processing, 2014, vol. 26, p. 425-430.Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://www.sciencedirect.com/science/article/pii/S1369800114002741Versió
info:eu-repo/semantics/publishedVersionParaules clau / Matèries
Resum
For this study, lead molybdate (PbMoO4) microcrystals were prepared by the co-precipitation method and processed using a conventional hydrothermal method at 100 °C for 10 min with polyvinyl alcohol (PVA) as the capping ... [+]
For this study, lead molybdate (PbMoO4) microcrystals were prepared by the co-precipitation method and processed using a conventional hydrothermal method at 100 °C for 10 min with polyvinyl alcohol (PVA) as the capping agent. These microcrystals were structurally characterized by X-ray diffraction (XRD) and micro-Raman spectroscopy, and their morphology was investigated by field-emission gun scanning electron microscopy (FEG-SEM). The optical properties were analyzed by ultraviolet–visible (UV–vis) absorption spectroscopy and photoluminescence (PL) measurements. XRD patterns and MR spectrum indicate that the PbMoO4 microcrystals have a scheelite-type tetragonal structure. FE-SEM images reveal that the PVA promotes the aggregation of several octahedrons and the formation of large porous stake-like PbMoO4 microcrystals which are related to the oriented attachment growth process. Moreover, the effect of the capping agent hinders the growth of a large amount of micro-octahedrons which can be verified with by several nanocrystals on large crystals. Intense green PL emission was observed at room temperature for PbMoO4 microcrystals which are related to structural defects at medium range and intermediary energy levels between the valence band (VB) and the conduction band (CB). Photocatalytic activity was observed for PbMoO4 as a catalyst in the degradation of the rhodamine B (RhB) dye, achieving total degradation after 90 min under UV-light. [-]
Publicat a
Materials Science in Semiconductor Processing, 2014, vol. 26Drets d'accés
Copyright © 2015 Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Apareix a les col.leccions
- QFA_Articles [825]