Morphology and barrier properties of solvent cast composites of thermoplastic biopolymers and purified cellulose fibers
Impacte
![Google Scholar](/xmlui/themes/Mirage2/images/uji/logo_google.png)
![Microsoft Academico](/xmlui/themes/Mirage2/images/uji/logo_microsoft.png)
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7034
comunitat-uji-handle3:10234/8619
comunitat-uji-handle4:
INVESTIGACIONAquest recurs és restringit
http://dx.doi.org/10.1016/j.carbpol.2007.05.041 |
Metadades
Títol
Morphology and barrier properties of solvent cast composites of thermoplastic biopolymers and purified cellulose fibersData de publicació
2008Editor
ElsevierISSN
1448617Cita bibliogràfica
Carbohydrate Polymers, 71, 2, p. 235-244Tipus de document
info:eu-repo/semantics/articleParaules clau / Matèries
Resum
This paper shows and discusses the morphology, thermal and transport properties of solvent cast biocomposites of poly(lactic acid) (PLA), polyhydroxybutyrate-co-valerate (PHBV) and polycaprolactones (PCL) containing ... [+]
This paper shows and discusses the morphology, thermal and transport properties of solvent cast biocomposites of poly(lactic acid) (PLA), polyhydroxybutyrate-co-valerate (PHBV) and polycaprolactones (PCL) containing purified alfa micro-cellulose fibers as a function of filler content. The SEM, optical microscopy and Raman imaging results indicate that a good dispersion of the fibers in the matrix was achieved for the three biopolymers. However, detrimental fiber agglomeration was clearly observed to take place for samples with fiber contents in excess of 5 wt%. The heat of fusion (related to crystallinity) of the semicrystalline PCL and PHBV biopolymers was seen to decrease, particularly in low fiber content biocomposites, but it seemed to increase slightly in the highly amorphous PLA biocomposites. In accordance with the morphology data, water and d-limonene direct permeability were seen to decrease to a significant extent in the biocomposites with low fiber contents. The permeability reduction was mostly related to a decrease in diffusivity but solubility was also found to be favorable. The main conclusion from this work is that purified cellulose fibers can also be used to enhance the barrier properties of thermoplastic biopolyesters of interest in, for instance, packaging and membrane applications. © 2007 Elsevier Ltd. All rights reserved. [-]
Drets d'accés
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
info:eu-repo/semantics/restrictedAccess
Apareix a les col.leccions
- ESID_Articles [480]
Referència a elsevier
![PDF](/xmlui/themes/Mirage2/images/uji/elsevier-pdf.png)