Compressive strength and microstructure of alkali-activated mortars with high ceramic waste content
Visualitza/
Impacte
Scholar |
Altres documents de l'autoria: Reig, Lucía; Sanz, M.A.; Borrachero, Mª Victoria; Monzó, J.; Soriano, Lourdes; PAYÁ, JORDI
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7035
comunitat-uji-handle3:10234/8617
comunitat-uji-handle4:
INVESTIGACIONMetadades
Títol
Compressive strength and microstructure of alkali-activated mortars with high ceramic waste contentData de publicació
2017-11Editor
ElsevierISSN
0272-8842; 1873-3956Cita bibliogràfica
REIG, L., et al. Compressive strength and microstructure of alkali-activated mortars with high ceramic waste content. Ceramics International, 2017, vol. 43, no 16, p. 13622-13634. MLATipus de document
info:eu-repo/semantics/articleVersió de l'editorial
Ceramics International, 2017, vol. 43, no 16Versió
info:eu-repo/semantics/submittedVersionParaules clau / Matèries
Resum
The present work investigated alkali-activated mortars with high ceramic waste contents. Tile ceramic waste (TCW) was used as both a recycled aggregate (TCWA) and a precursor (TCWP) to obtain a binding matrix by the ... [+]
The present work investigated alkali-activated mortars with high ceramic waste contents. Tile ceramic waste (TCW) was used as both a recycled aggregate (TCWA) and a precursor (TCWP) to obtain a binding matrix by the alkali-activation process. Mortars with natural siliceous (quartz) and calcareous (limestone) aggregates, and with other ceramic waste materials (red clay brick RCB and ceramic sanitaryware CSW waste), were also prepared for comparison purposes. Given the lower density and higher water absorption values of the ceramic aggregates, compared to the natural ones, it was necessary to adapt the preparation process of the recycled mortars by presaturating the aggregate with water before mixing with the TCWP alkali-activated paste. Aggregate type considerably determined the mechanical behaviour of the samples cured at 65 °C for 3 days. The mortars prepared with the siliceous aggregate presented poor mechanical properties, even when cured at 65 °C. The behaviour of the limestone aggregate mortars depended heavily on the applied curing temperature and, although they presented the best mechanical properties of all those cured at room temperature, their compressive strength reached a maximum when cured at 65 °C, and then decreased. The mechanical properties of the mortars prepared with TCWA progressively increased with curing time (53 MPa at 65 °C for 28 days). An optimum 50 wt% proportion was observed for the limestone/TCWA mortars (≈43 MPa, 3 days at 65 °C), whereas the mechanical properties of that prepared with siliceous particles (10 MPa) progressively increased with the TCWA content, up to 100 wt% substitution (23 MPa). Limestone particles interacted with the binding matrix, and played an interesting beneficial role at the 20 °C curing temperature, with a slight reduction when cured long term (28 days) at 65 °C. The results demonstrated a potential added value for these ceramic waste materials. [-]
Proyecto de investigación
Spanish Ministry of Science and Innovation / GEOCEDEM BIA 2011-26947; Spanish Ministry of Economy and Competitiveness / BIA2015 70107-R; FEDERDrets d'accés
Copyright © Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
Apareix a les col.leccions
- EMC_Articles [823]