One step hydrothermal synthesis of LaFeO3 perovskite
Ver/ Abrir
Impacto
Scholar |
Otros documentos de la autoría: Gómez-Cuaspud, Jairo. A.; Vera-López, Enrique; Carda Castelló, Juan Bautista; BARRACHINA ALBERT, ESTER
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONMetadatos
Título
One step hydrothermal synthesis of LaFeO3 perovskiteAutoría
Fecha de publicación
2017Editor
Akadémiai Kiadó. Springer Verlag (Germany)ISSN
1878-5190; 1878-5204Cita bibliográfica
Gómez-Cuaspud, J.A., Vera-López, E., Carda-Castelló, J.B. et al. Reac Kinet Mech Cat (2017) 120: 167-179Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://link.springer.com/article/10.1007/s11144-016-1092-8Palabras clave / Materias
Resumen
This work describes the synthesis of LaFeO3 oxide, using a one-step hydrothermal synthesis route, to obtain a solid exhibiting superficial, morphological and textural properties useful for potential applications. The ... [+]
This work describes the synthesis of LaFeO3 oxide, using a one-step hydrothermal synthesis route, to obtain a solid exhibiting superficial, morphological and textural properties useful for potential applications. The synthesis process starts from corresponding metal nitrates of lanthanum and iron in well-defined concentration and KOH as mineralizing agent. The reaction is developed in a Teflon-lined stainless steel autoclave at 300 °C for 14 days. The composition and surface area were determined with X-ray fluorescence (XRF) and nitrogen adsorption isotherms (BET), verifying the obtaining of a stoichiometric, high, and active phase of oxide. The crystalline structure was evaluated with X-ray diffraction analysis (XRD), showing a pure orthorhombic perovskite phase. TPR results show the development of three single steps at different temperatures, kinetically detectable and related with reduction of component oxides. Scanning and transmission electron microscopy (SEM-TEM) results showed a remarkable degree of crystallization, favouring a specific morphology as a result of the low consolidation temperature of the perovskite phase. Catalytic test by means of methane reaction, performed along 240 on stream, reveals a light deactivation rate, decreasing progressively 7.1% until 60% of methane conversion, indicating the improved morphological and surface characteristics for potential applications. [-]
Publicado en
GÓMEZ-CUASPUD, Jairo A., et al. One-step hydrothermal synthesis of LaFeO3 perovskite for methane steam reforming. Reaction Kinetics, Mechanisms and Catalysis, 2017, vol. 120, núm. 1Derechos de acceso
© Akadémiai Kiadó, Budapest, Hungary 2016
"The final publication is available at Springer via http://dx.doi.org/10.1007/s11144-016-1092-8"
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
Aparece en las colecciones
- QUIO_Articles [699]