Solvothermal synthesis of Eu3+-doped holmium aluminum garnet
comunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONAquest recurs és restringit
http://dx.doi.org/10.1016/j.mencom.2015.09.024 |
Metadades
Títol
Solvothermal synthesis of Eu3+-doped holmium aluminum garnetData de publicació
2015Editor
ElsevierISSN
0959-9436Cita bibliogràfica
PAVASARYTE, Lina; JULIÁN LÓPEZ, Beatriz; KAREIVA, Aivaras. Solvothermal synthesis of Eu 3+-doped holmium aluminum garnet. Mendeleev Communications, 2015, vol. 25, no 5, p. 384-385.Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://www.sciencedirect.com/science/article/pii/S0959943615001820Paraules clau / Matèries
Resum
Eu3+-doped holmium aluminum garnet (Ho3Al5O12, HoAG) has been synthesized by a solvothermal method and annealed at various temperatures. The X-ray diffraction patterns confirmed that single-phase HoAG was obtained ... [+]
Eu3+-doped holmium aluminum garnet (Ho3Al5O12, HoAG) has been synthesized by a solvothermal method and annealed at various temperatures. The X-ray diffraction patterns confirmed that single-phase HoAG was obtained already at 220°C. [-]
Publicat a
Mendeleev Communications, 2015, vol. 25, no 5Drets d'accés
Copyright © Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Apareix a les col.leccions
- QUIO_Articles [702]