Pink ceramic pigments based on chromium doped M(Al2-xCrx)O-4, M = Mg, Zn, normal spinel
Impacto
Scholar |
Otros documentos de la autoría: Prim, S. R.; García López, Araceli; Galindo Llorach, Roberto; Cerro Lloria, Sara; Llusar, Mario; Folgueras, M. V.; Monrós, Guillermo
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONEste recurso está restringido
http://dx.doi.org/10.1016/j.ceramint.2013.02.035 |
Metadatos
Título
Pink ceramic pigments based on chromium doped M(Al2-xCrx)O-4, M = Mg, Zn, normal spinelAutoría
Fecha de publicación
2013-08Editor
ElsevierISSN
0272-8842Cita bibliográfica
PRIM, S. R., et al. Pink ceramic pigments based on chromium doped M (Al< sub> 2− x</sub> Cr< sub> x</sub>) O< sub> 4</sub>, M Mg, Zn, normal spinel. Ceramics International, 2013, vol. 39, no 6, p. 6981-6989Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://www.sciencedirect.com/science/article/pii/S027288421300196X#Palabras clave / Materias
Resumen
In this paper M(Al2−xCrx)O4, MMg, Zn and x from 0.05 to 2 compositions, have been prepared by solid state reaction in order to analyse their reactivity, structure, limit of solid solution, stability and pigmenting ... [+]
In this paper M(Al2−xCrx)O4, MMg, Zn and x from 0.05 to 2 compositions, have been prepared by solid state reaction in order to analyse their reactivity, structure, limit of solid solution, stability and pigmenting properties in conventional ceramic glazes. Solid solutions are obtained at 1200 °C in the Zn case (gahnite) and at 1400 °C in the Mg case (magnesium spinel). In both cases powders become pink coloured up to x=0.4 and then progressively greenish. Likewise powders glazed in a conventional ceramic glaze matrix of the CaOZnOSiO2 system for double firing stoneware (1050 °C) produce glazes firstly orange coloured up to x=0.4, pink up to x=1.2 and finally green at higher x. The colour evolution is associated to the entrance at low doping levels of relatively big Cr3+ (0.755 Å) substituting Al3+ (0.675 Å) in VI coordinated sites of both spinel lattices; this produces an enhancement of the crystal field strength under the VI coordinated Cr3+ that shifts the light absorbances to higher energy and an orange-pink colour can be observed. But when the entrance of Cr3+ progresses, the crystal field strength under the ion relaxes and absorption bands shift to higher wavelength when x increases, producing green colours. The UV–vis–NIR spectra of low x pink M(Al2−xCrx)O4 compositions are similar to those of ruby (Cr0.1Al1.9)O3, indicating analogous mechanism of colour. [-]
Publicado en
Ceramics International, 2013, vol. 39, no 6Derechos de acceso
Copyright © 2014 Elsevier B.V. except certain content provided by third parties. ScienceDirect® is a registered trademark of Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Aparece en las colecciones
- QUIO_Articles [689]