Fracture toughness and temperature dependence of Young's modulus of a sintered albite glass
Visualitza/
Impacte
Scholar |
Altres documents de l'autoria: Dal Bó, Marcelo; Cantavella Soler, Vicente; Sánchez-Vilches, Enrique; Hotza, Dachamir; Gilabert Villegas, Francisco A.
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7033
comunitat-uji-handle3:10234/8618
comunitat-uji-handle4:
INVESTIGACIONMetadades
Títol
Fracture toughness and temperature dependence of Young's modulus of a sintered albite glassAutoria
Data de publicació
2013-03Editor
ElsevierCita bibliogràfica
DAL BÓ, Marcelo, et al. Fracture toughness and temperature dependence of Young's modulus of a sintered albite glass. Journal of Non-Crystalline Solids, 2013, 363: 70-76.Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://www.sciencedirect.com/science/article/pii/S0022309312007090Versió
info:eu-repo/semantics/submittedVersionParaules clau / Matèries
Resum
Albite glass is an important component in many ceramic compositions, often used as liquid phase during the sintering process. Nevertheless, in spite of its almost ubiquous presence in the final microstructure of these ... [+]
Albite glass is an important component in many ceramic compositions, often used as liquid phase during the sintering process. Nevertheless, in spite of its almost ubiquous presence in the final microstructure of these compositions, some properties such as Young's modulus or fracture toughness have not been extensively studied in literature. This paper presents an experimental study on a sintered albite glass obtained from sodium feldspar powder. The microstructure of the resultant amorphous solid was analyzed via scanning electron microscopy and X-ray diffraction. Fracture toughness was determined at room temperature from the critical stress intensity factor (KIC) with a three point bending single-edge notched test (SENB). Young's modulus and coefficient of thermal expansion (CTE) were measured as a function of the temperature. A value of CTE of 6.6 × 10− 6 °C− 1 within the temperature range 300–500 °C was found. Young's modulus values of the albite glass were within the range from 63.6 to 65.2 MPa. SENB tests revealed a fracture toughness of KIC = 0.78 ± 0.06 MPa m1/2, which is of similar value to those found for borosilicate and soda-lime glasses. [-]
Publicat a
Journal of Non-Crystalline Solids Volume 363, 1 March 2013, Pages 70–76Drets d'accés
http://rightsstatements.org/vocab/CNE/1.0/
info:eu-repo/semantics/openAccess
info:eu-repo/semantics/openAccess
Apareix a les col.leccions
- QUI_Articles [296]