Stability of ceramic glaze compositions. Correlation between partial dissolution and rheological properties. Part 1
Impacto
Scholar |
Otros documentos de la autoría: Gazulla Barreda, Maria Fernanda; Barba-Juan, Antonio; Orduña, Mónica; Bautista, Y.
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7033
comunitat-uji-handle3:10234/8618
comunitat-uji-handle4:
INVESTIGACIONEste recurso está restringido
http://www.ingentaconnect.com/content/sgt/gt/2012/00000053/00000003/art00002 |
Metadatos
Título
Stability of ceramic glaze compositions. Correlation between partial dissolution and rheological properties. Part 1Fecha de publicación
2012Editor
Society of Glass TechnologyCita bibliográfica
GAZULLA, M. F., et al. Stability of ceramic glaze compositions. Correlation between partial dissolution and rheological properties. Part 1. Glass Technology-European Journal of Glass Science and Technology Part A, 2012, 53.3: 101-108Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://www.ingentaconnect.com/content/sgt/gt/2012/00000053/00000003/art00002Palabras clave / Materias
Resumen
When glaze compositions are prepared as aqueous suspensions, the frit is wet milled in an alumina ball mill with additives and water to obtain a glaze suspension with the appropriate rheological properties for subsequent ... [+]
When glaze compositions are prepared as aqueous suspensions, the frit is wet milled in an alumina ball mill with additives and water to obtain a glaze suspension with the appropriate rheological properties for subsequent application. Viscosity of the suspension is usually adjusted by adding deflocculants, binders and suspension agents. This paper examines the partial dissolution of Si, B, Ca, Mg, and Zn in glaze suspensions that contain a zirconium white frit, using two deflocculants (a sodium tripolyphosphate and a sodium polyacrylate), under different operating conditions (dry milling the frit in a jet mill and wet milling the frit in an alumina ball mill). Samples were taken at different times to study the ageing of the glaze suspension: the elements in the liquid fraction of the glaze suspension were analysed and a rheological study of the prepared suspensions was conducted. Partial dissolution of the frit was then related to the change in rheological properties. Viscosity was found to vary with time. Further tests were subsequently conducted in which a calcium salt was added to a sodium carboxymethylcellulose (CMC) solution. The variation in viscosity was found to be caused by a change in dissolved CMC behaviour, which could be due to a change in CMC molecular conformation. [-]
Publicado en
Glass Technology - European Journal of Glass Science and Technology Part A, Volume 53, Number 3, June 2012Derechos de acceso
http://rightsstatements.org/vocab/CNE/1.0/
info:eu-repo/semantics/restrictedAccess
info:eu-repo/semantics/restrictedAccess
Aparece en las colecciones
- QUI_Articles [296]