New insights on the structural and optical properties of Ce–Ti mixed oxide nanoparticles doped with praseodymium
Ver/ Abrir
Impacto
Scholar |
Otros documentos de la autoría: Fernández González, Ricardo; Julian-Lopez, Beatriz; Cordoncillo, Eloisa; Escribano López, Purificación
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONMetadatos
Título
New insights on the structural and optical properties of Ce–Ti mixed oxide nanoparticles doped with praseodymiumAutoría
Fecha de publicación
2010-10-26Editor
Royal Society of ChemistryISSN
0959-9428; 1364-5501Cita bibliográfica
Journal of Materials Chemistry (2011) no. 21, p. 497-504Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://pubs.rsc.org/en/content/articlepdf/2011/jm/c0jm01625jPalabras clave / Materias
Resumen
Nanostructured, doped Ce–Ti mixed oxides are potential materials for several applications such as pigments, catalysis, fuel cells, optical films, and gas sensors. In this article, a series of Pr-doped Ce–Ti oxides ... [+]
Nanostructured, doped Ce–Ti mixed oxides are potential materials for several applications such as pigments, catalysis, fuel cells, optical films, and gas sensors. In this article, a series of Pr-doped Ce–Ti oxides have been prepared by the solvothermal method. These compounds were characterized by XRD, Raman, N2 sorption, SEM and UV–VIS spectrophotometry techniques. The experimental results suggest that spherical morphology, nanocrystalline particles and high specific surface area (up to
180 m2 g-1) are achieved at low temperature with this free surfactant methodology. Under basic conditions, a single phase product is identified at high temperature (1000 ºC), while for acid or neutral conditions, secondary phases appear. Different colored materials, ranging from yellow to red, are obtained by varying the firing temperature, quantity of doping praseodymium and the pH of the reaction. The chemical stability of these oxides was tested in some industrial polymers or glazes. [-]
Derechos de acceso
© Royal Society of Chemistry
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
Aparece en las colecciones
- QUIO_Articles [690]