Microstructure assessment of suspension plasma spraying coatings from multicomponent submicronic Y-TZP/Al2O3/SiC particles
Visualitza/
Impacte
Scholar |
Altres documents de l'autoria: Carnicer Cervera, Víctor; Orts Tarí, María José; Moreno, Rodrigo; Sánchez-Vilches, Enrique
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/176601
comunitat-uji-handle3:10234/176618
comunitat-uji-handle4:
INVESTIGACIONMetadades
Títol
Microstructure assessment of suspension plasma spraying coatings from multicomponent submicronic Y-TZP/Al2O3/SiC particlesData de publicació
2018-08-01Editor
ElsevierISSN
0272-8842Cita bibliogràfica
CARNICER, Víctor, et al. Microstructure assessment of suspension plasma spraying coatings from multicomponent submicronic Y-TZP/Al2O3/SiC particles. Ceramics International, 2018, vol. 44, no 11, p. 12014-12020Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
https://www.sciencedirect.com/science/article/pii/S0272884218307521Versió
info:eu-repo/semantics/draftParaules clau / Matèries
Resum
In this research, Suspension Plasma Spraying (SPS) technique was used for the thermal deposition of a multicomponent mixture made up of an Y-TZP/Al2O3 matrix with SiC particles. Two suspensions of Y-TZP and Al2O3 with ... [+]
In this research, Suspension Plasma Spraying (SPS) technique was used for the thermal deposition of a multicomponent mixture made up of an Y-TZP/Al2O3 matrix with SiC particles. Two suspensions of Y-TZP and Al2O3 with different SiC particles content (6 wt% and 12 wt%) were tested as feedstocks in the SPS process. Three stand-off distances were varied in order to assess coating microstructure and evaluate the presence of SiC in the final coatings. Coatings were characterised in terms of porosity, microstructure and phase distribution. The estimate of the amount of SiC in the coating was carried out by XRD technique.
Findings showed typical cauliflower-like SPS microstructure which intensifies with stand-off distance. Coatings porosity varied significantly between 8% and 25% whereas minimum porosity was found for the intermedium stand-off distance of 40 mm.
Microstructure analysis also revealed the presence of SiC particles in the coatings which was confirmed by EDX analysis, overall XRD tests as well as TG analysis. Finally, evaluation of SiC content in the final coatings by means of XRD analysis showed that most of SiC particles (c.a 80%) of the feedstocks were preserved in the final coatings. [-]
Publicat a
Ceramics International, 2018, vol. 44, no 11Drets d'accés
Copyright © Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
Apareix a les col.leccions
- ITC_Articles [74]