Thermal behaviour of multilayer and functionally-graded YSZ/Gd2Zr2O7 coatings
Ver/ Abrir
Impacto
Scholar |
Otros documentos de la autoría: Carpio Cobo, Pablo; Salvador Moya, María Dolores; Borrell, A.; Sánchez-Vilches, Enrique
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7033
comunitat-uji-handle3:10234/8618
comunitat-uji-handle4:
INVESTIGACIONMetadatos
Título
Thermal behaviour of multilayer and functionally-graded YSZ/Gd2Zr2O7 coatingsFecha de publicación
2017Editor
ElsevierISSN
0272-8842; 1873-3956Cita bibliográfica
CARPIO, P., et al. Thermal behaviour of multilayer and functionally-graded YSZ/Gd 2 Zr 2 O 7 coatings. Ceramics International, 2017, vol. 43, no 5, p. 4048-4054. MLATipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://www.sciencedirect.com/science/article/pii/S0272884216321927Versión
info:eu-repo/semantics/submittedVersionPalabras clave / Materias
Resumen
Zirconates with pyrochlore structure, such as Gd2Zr2O7, are new promising thermal barrier coatings because of their very low thermal conductivity and good chemical resistance against molten salts. However, their ... [+]
Zirconates with pyrochlore structure, such as Gd2Zr2O7, are new promising thermal barrier coatings because of their very low thermal conductivity and good chemical resistance against molten salts. However, their coefficient of thermal expansion is low, therefore their thermal fatigue resistance is compromised. As a solution, the combination of yttria-stabilised zirconia (YSZ) and Gd2Zr2O7 can reduce the thermal contraction mismatch between the thermal barrier coating parts.
In the present study, two possible designs have been performed to combine YSZ/Gd2Zr2O7. On the one hand, a multilayer coating was obtained where YSZ layer was deposited between a Gd2Zr2O7 layer and a bond coat. On the other hand, a functionally-graded coating was designed where different layers with variable ratios of YSZ/Gd2Zr2O7 were deposited such that the composition gradually changed along the coating thickness.
Multilayer and functionally-graded coatings underwent isothermal and thermally-cycled treatments in order to evaluate the oxidation, sintering effects and thermal fatigue resistance of the coatings. The YSZ/Gd2Zr2O7 multilayer coating displayed better thermal behaviour than the Gd2Zr2O7 monolayer coating but quite less thermal fatigue resistance compared to the conventional YSZ coating. However, the functionally-graded coating displays a good thermal fatigue resistance. Hence, it can be concluded that this kind of design is ideal to optimise the behaviour of thermal barrier coatings. [-]
Publicado en
Ceramics International, 2017, vol. 43, no 5Derechos de acceso
Copyright © Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
Aparece en las colecciones
- QUI_Articles [296]