Ceria-doped scandia-stabilized zirconia (10Sc2O3·1CeO2·89ZrO2) as electrolyte for SOFCs: Sintering and ionic conductivity of thin, flat sheets
Ver/ Abrir
Impacto
Scholar |
Otros documentos de la autoría: Escardino Benlloch, Agustín; Belda Peña, Adriana; Orts Tarí, María José; Gozalbo Nebot, Ana
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7033
comunitat-uji-handle3:10234/8618
comunitat-uji-handle4:
INVESTIGACIONMetadatos
Título
Ceria-doped scandia-stabilized zirconia (10Sc2O3·1CeO2·89ZrO2) as electrolyte for SOFCs: Sintering and ionic conductivity of thin, flat sheetsFecha de publicación
2017-03Editor
Wiley; The American Ceramic SocietyCita bibliográfica
Escardino A, Belda A, Orts M-J, Gozalbo A. 10Sc2O3·1CeO2·89ZrO2 as electrolyte for SOFCs: Sintering and ionic conductivity of thin, flat sheets. Int J Appl Ceram Technol. 2017;00:1-11. https://doi.org/10.1111Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://onlinelibrary.wiley.com/doi/10.1111/ijac.12675/fullVersión
info:eu-repo/semantics/acceptedVersionPalabras clave / Materias
Resumen
In this study, thin, flat sheets, about 90 μm thick, were prepared from ceria-doped scandia-stabilized zirconia with molecular formula 10Sc2O3·1CeO2·89 ZrO2 (10Sc1CeSZ) by tape casting and subsequent sintering at ... [+]
In this study, thin, flat sheets, about 90 μm thick, were prepared from ceria-doped scandia-stabilized zirconia with molecular formula 10Sc2O3·1CeO2·89 ZrO2 (10Sc1CeSZ) by tape casting and subsequent sintering at different thermal cycles. A sintering thermal cycle was selected that yielded defect-free flat sheets, with practically negligible porosity (between 0.35% and 0.10%) and average grain diameters ranging from 1.32 to 6.30 μm. Ionic conductivity at 600°C was as high as 21 mS/cm. Ionic conductivity increased with average grain diameters up to 2.7 μm. At higher average grain diameters, conductivity remained practically constant. [-]
Publicado en
Int J Appl Ceram Technol. 2017Derechos de acceso
© 2017 The American Ceramic Society
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
Aparece en las colecciones
- QUI_Articles [300]