Structural characterization and colour of Ni3VxP2−xO8 (0 ≤ x ≤ 2) and Ni2VyP2−yO7 (0 ≤ y ≤ 2) materials
Visualitza/
Impacte
Scholar |
Altres documents de l'autoria: Tena, M. A.; Mendoza, Rafael; García, José R.; Garcia-Granda, Santiago
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONMetadades
Títol
Structural characterization and colour of Ni3VxP2−xO8 (0 ≤ x ≤ 2) and Ni2VyP2−yO7 (0 ≤ y ≤ 2) materialsData de publicació
2017Editor
ElsevierISSN
2211-3797Cita bibliogràfica
TENA, M. A., et al. Structural characterization and colour of Ni 3 V x P 2− x O 8 (0≤ x≤ 2) and Ni 2 V y P 2− y O 7 (0≤ y≤ 2) materials. Results in Physics, 2017Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://www.sciencedirect.com/science/article/pii/S2211379717300220Versió
info:eu-repo/semantics/publishedVersionParaules clau / Matèries
Resum
Structural characterization of Ni3VxP2−xO8 (0 ≤ x ≤ 2) and Ni2VyP2−yO7 (0 ≤ y ≤ 2) compositions was made and colour parameters of these materials measured. Ni(II) diphosphate and divanadate crystalline phases are not ... [+]
Structural characterization of Ni3VxP2−xO8 (0 ≤ x ≤ 2) and Ni2VyP2−yO7 (0 ≤ y ≤ 2) compositions was made and colour parameters of these materials measured. Ni(II) diphosphate and divanadate crystalline phases are not stables at high temperature. Solid solutions in Ni3P2O8 and Ni3V2O8 are obtained by incorporation of V(V) in Ni orthophosphate and P(V) in Ni orthovanadate structures. Solid solutions with Ni3V2O8 structure are formed in a greater compositional interval than solid solutions with Ni3P2O8 structure. These materials might be used as ceramic pigments because of its thermal and chemical stability. Tan brown colorations were obtained in glazed tiles when the fired compositions were 4% weight enamelled with a commercial glaze. [-]
Publicat a
Results in Physics, 2017, vol. 7Drets d'accés
info:eu-repo/semantics/openAccess
Apareix a les col.leccions
- QUIO_Articles [705]
Els següents fitxers sobre la llicència estan associats a aquest element: