Potencialidad de un residuo de frita procedente del sector cerámico como materia prima para la producción de material vitrocerámico
Visualitza/
Impacte
Scholar |
Altres documents de l'autoria: BARRACHINA ALBERT, ESTER; Llop Pla, Jorge; Notari Abad, María Dolores; Carda Castelló, Juan Bautista
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7053
comunitat-uji-handle3:10234/8639
comunitat-uji-handle4:
INVESTIGACIONMetadades
Títol
Potencialidad de un residuo de frita procedente del sector cerámico como materia prima para la producción de material vitrocerámicoAutoria
Data de publicació
2015-05Editor
Elsevier; Sociedad Española de Cerámica y VidrioISSN
0366-3175Cita bibliogràfica
ALBERT, Ester Barrachina, et al. Potencialidad de un residuo de frita procedente del sector cerámico como materia prima para la producción de material vitrocerámico. Boletín de la Sociedad Española de Cerámica y Vidrio, 2015, vol. 54, no 3, p. 101-108.Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://www.sciencedirect.com/science/article/pii/S0366317515000412Paraules clau / Matèries
Resum
This work consists of studying the devitrification capacity of a residue from sodium-calcium frit, using the vitreous powder sintering method, which follows the traditional ceramic processing route, including a specific ... [+]
This work consists of studying the devitrification capacity of a residue from sodium-calcium frit, using the vitreous powder sintering method, which follows the traditional ceramic processing route, including a specific heat treatment to generate the appearance of crystals from the original glass phase. Initially the frit residue has been characterized by instrumental techniques such as XRF, XRD and DTA/TG. Furthermore, the chemical analysis (XRF) has allowed the prediction of devitrification potentiality of this residue by theoretical approaches represented by Gingsberg, Raschin-Tschetverikov and Lebedeva ternary diagrams. Then, this residue was subjected to traditional ceramic method, by changing the grinding time, the pressing pressure and prepared samples were obtained at different temperatures. In this part, the techniques for measuring particle size by laser diffraction and XRD and SEM to evaluate the generated crystalline phases, were applied. Finally, it has been found that this frit residue works as glass-ceramic precursor, devitrifying in wollastonite crystals as majority phase and without being subjected to the melting step of the glass-ceramic typical method. [-]
Publicat a
Boletín de la Sociedad Española de Cerámica y Vidrio, 2015, vol. 54, no 3Drets d'accés
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/openAccess
info:eu-repo/semantics/openAccess
Apareix a les col.leccions
- QUIO_Articles [690]