Thermodynamic and electronic study of Ga1−xMnxN films. A theoretical study
Impacto
Scholar |
Otros documentos de la autoría: Gomes, M. C.; Leite, D. M. G.; Sambrano, Julio; Dias da Silva, J. H.; De Souza, A. R.; Beltran, Armando
Metadatos
Mostrar el registro completo del ítemcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7013
comunitat-uji-handle3:10234/8638
comunitat-uji-handle4:
INVESTIGACIONEste recurso está restringido
http://dx.doi.org/ 10.1016/j.susc.2011.05.007 |
Metadatos
Título
Thermodynamic and electronic study of Ga1−xMnxN films. A theoretical studyAutoría
Fecha de publicación
2011-05-14Editor
ElsevierISSN
0039-6028Cita bibliográfica
Surface Science (Aug. 2011) vol. 605, no. 15-16, p. 1431-1437Tipo de documento
info:eu-repo/semantics/articleVersión de la editorial
http://www.sciencedirect.com/science/article/pii/S0039602811001841Versión
info:eu-repo/semantics/publishedVersionPalabras clave / Materias
Resumen
Periodic slab calculations based on density functional theory were performed at the B3LYP level to gain insight
into the surfaces of wurtzite GaN nanostructures. The (1010) and (1120) GaN surfaces are the most
the ... [+]
Periodic slab calculations based on density functional theory were performed at the B3LYP level to gain insight
into the surfaces of wurtzite GaN nanostructures. The (1010) and (1120) GaN surfaces are the most
thermodynamically stable surfaces, the energy of the former being slightly smaller than that of the latter. The
thermodynamic stability associated with the equilibrium shape of nanowires was determined using the
calculated values.
Doping with Mn further decreases the surface energy of (1010) and (1120). The minimum surface energy of
Ga1−xMnxN (0.04≤x≤0.17) is found at x ~ 0.08, for (1010) and (1120) slab models. Substitution of Ga with
Mn in different positions relative to the surface shows that the total energy increases as the Mn atoms move
from the surface layer to the interior sites of the slabs. Mn doping is also responsible for decreases in the band
gap energy: the minimum calculated band gap in the Ga1−xMnxN (1010) slab was found at x ~ 0.17, whereas
the (1120) surface presented the corresponding minimum at x ~ 0.04. The magnetic moments associated with
Mn were observed to increase as the ion positions moved closer to the surfaces. [-]
Derechos de acceso
© 2011 Elsevier Inc. All rights reserved
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Aparece en las colecciones
- QFA_Articles [812]