Influence of the activator concentration and calcium hydroxide addition on the properties of alkali-activated porcelain stoneware
Impacte
Scholar |
Altres documents de l'autoria: Reig, Lucía; Soriano, Lourdes; Borrachero, Mª Victoria; Monzó, J.; PAYÁ, JORDI
Metadades
Mostra el registre complet de l'elementcomunitat-uji-handle:10234/9
comunitat-uji-handle2:10234/7035
comunitat-uji-handle3:10234/8617
comunitat-uji-handle4:
INVESTIGACIONAquest recurs és restringit
http://dx.doi.org/10.1016/j.conbuildmat.2014.04.023 |
Metadades
Títol
Influence of the activator concentration and calcium hydroxide addition on the properties of alkali-activated porcelain stonewareData de publicació
2014-07Editor
ElsevierISSN
0950-0618Tipus de document
info:eu-repo/semantics/articleVersió de l'editorial
http://www.sciencedirect.com/science/article/pii/S0950061814003407Paraules clau / Matèries
Resum
Objective
The aim of this research was to investigate the influence of the alkali activator concentration and calcium dosage on the fresh behavior, compressive strength and microstructure of the binder produced by ... [+]
Objective
The aim of this research was to investigate the influence of the alkali activator concentration and calcium dosage on the fresh behavior, compressive strength and microstructure of the binder produced by the alkali activation of porcelain stoneware waste, using NaOH and sodium silicate solution as activators.
Materials
Porcelain stoneware waste, NaOH and sodium silicate.
Method
Tested properties of mortars were the compressive strength and the setting times. Thermogravimetric analyses, microscopic studies, pH measurements, XRD and FTIR tests were used to assess the evolution of the microstructure developed.
Results
The results show that the activator concentration and calcium to sodium molar ratio strongly influence the fresh behavior and the hardening process of mortars. A linear evolution of compressive strength with sodium addition was observed when keeping the SiO2 concentration constant. Mortar samples with up to 36 MPa under compression were obtained after curing for 7 days at 65 °C. [-]
Publicat a
Construction and Building Materials, 2014, vol. 63Drets d'accés
Copyright © 2014 Elsevier Ltd. All rights reserved.
Copyright © 2015 Elsevier B.V. or its licensors or contributors. ScienceDirect® is a registered trademark of Elsevier B.V.
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
http://rightsstatements.org/vocab/InC/1.0/
info:eu-repo/semantics/restrictedAccess
Apareix a les col.leccions
- EMC_Articles [807]