Several ceramic pigments based on Cr-doped Mg0.5FeTi1.5O5 (“ferrian armalcolite”) solid solutions were prepared by the solid-state (ceramic) route, with the aim to investigate the effect of Cr-doping on the resulting reddish or dark-brown color, as well as its coloring performance as ceramic pigments or dyes in conventional low-temperature ceramic glazes.
For this purpose, two different doping schemes were formulated (Arm1 series: Mg0.5-x(Fe1Cr2x)Ti1.5-xO5, with x=0-0.25, in which Cr3+ is expected to replace both Ti4+ and Mg2+ ions; and Arm2 series: Mg0.5(Fe1-xCrx)Ti1.5O5, with x=0-0.5, in which Cr3+ is replacing exclusively Fe3+ ions).
The samples were calcined in industrial-like firing conditions up to 1000°C and 1200 °C (3 h soaking), and the resulting powders were characterized by XRD (formation of solid solution and cell parameters measurement) and UV-vis-NIR spectroscopy (optical spectra and CIE-L*a*b* parameters of fired powders and of samples enameled within two different ceramic glazes).
XRD results showed that at 1000 °C is observed that the increase of Cr doping is accompanied by a larger amount of secondary phases. This indicates that with a quickly thermal treatment (3 h/ 1000 °C) an armalcolite phase is not still stabilized by entropy. Remarkably, the increase of firing temperature from 1000 °C to 1200 °C leads to an important increase of reactivity in both series (Arm 1 and Arm2). In effect, at 1200 °C in the case of Arm1 series, the armalcolite phase appears almost as single phase from x=0 to x=0.1, with only a very small and almost negligible quantity of residual rutile. A monophasic system of armalcolite is not formed in ARM1Cr0.25 at 1200 °C. In contrast, Arm2 series, in which Cr3+ is replacing exclusively by Fe3+ ions, gets stabilize the solid solution of armalcolite.
On the other hand, UV-vis-NIR results showed that is very difficult to distinguish the presence of Cr3+ or Cr4+ in an octahedral sites in samples containing Fe3+ ions in these positions simultaneously, because the bands of Cr3+ and Cr4+ are overlapped to a high extent with the absorption bands of iron (III).
eng
Grau en Química
Grado en Química
Bachelor's Degree in Chemistry
Solid-state synthesis and characterization of ceramic pigments based on Cr-doped Mg0.5FeTi1.5O5 armalcolites
info:eu-repo/semantics/bachelorThesis
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
URL
https://repositori.uji.es/xmlui/bitstream/10234/163942/1/TFG_2015_ripollesM.pdf
File
MD5
3269aed4de69a43211ae70d44cb4b76a
2118696
application/pdf
TFG_2015_ripollesM.pdf
URL
https://repositori.uji.es/xmlui/bitstream/10234/163942/7/TFG_2015_ripollesM.pdf.txt
File
MD5
7971605cf4c35bf32a218b16d9538ef4
63686
text/plain
TFG_2015_ripollesM.pdf.txt